New strategy for osseodensification during osteotomy in low

Scientific Reports volume 13, Article number: 11924 (2023) Cite this article

221 Accesses

1 Altmetric

Metrics details

The goal of this in vitro study was to evaluate and propose a new strategy for osseodensification technique using a drill counterclockwise to densification of bone of low density. Synthetic bone blocks of two different low densities (type III and IV) were used for the tests. The conventional drilling group (CD group) used Turbo-drill in a clockwise direction, and the osseodensification group (OD group) applied Turbo-drill in a counterclockwise direction. The applied tests were: (i) measurement of the temperature variation (ΔT) and (ii) measurement of the torque during the osteotomies, comparing the new strategy with the conventional drilling. Both groups were tested without (condition c1) and with (condition c2) irrigation, generating four subgroups: CDc1, CDc2, ODc1, and ODc2. Twenty osteotomies were made for each subgroup with a thermocouple positioned intra-bone (1 mm distant from the osteotomy) to measure the temperature produced. Other 20 samples/group were used to measure the torque value during each osteotomy in both synthetic bone density blocks. The mean of the ΔT during the osteotomies in type III bone was: 6.8 ± 1.26 °C for the CDc1 group, 9.5 ± 1.84 °C for the ODc1, 1.5 ± 1.35 °C for the CDc2, and 4.5 ± 1.43 °C for ODc2. Whereas, in the type IV bone, the ΔT was: 5.2 ± 1.30 °C for the CDc1 group, 7.0 ± 1.99 °C for the ODc1, 0.9 ± 1.05 °C for the CDc2, and 2.7 ± 1.30 °C for ODc2. The maximum torque during the osteotomies was: 8.8 ± 0.97 Ncm for CD samples and 11.6 ± 1.08 Ncm for OD samples in the type III bone; and 5.9 ± 0.99 Ncm for CD samples and 9.6 ± 1.29 Ncm for OD samples in the type IV bone. Statistical differences between the groups were detected in tests and conditions analyzed (p < 0.05). Using the drill counterclockwise for osseodensification in low-density bone generated a significantly greater torque of a drill than in CD and temperature variation during osteotomies. However, the temperature range displayed by the OD group was below critical levels that can cause damage to bone tissue.

Endosteal implants' use to rehabilitate missing teeth has become widely used in modern dentistry, mainly due to their predictability and long-term results1,2,3. With the advancement of biological knowledge of processes related to osseointegration of implants, new techniques have emerged to help and/or enable the use of implants in areas with some type of bone deficiency, whether in volume or density. Frequently, bone ridges healed after tooth loss are characterized by low density due to the lack of internal stimuli for a period, which may make the initial stabilization of a dental implant difficult. To better enable the initial stability of implants in those areas, some techniques have been proposed and applied, such as under-drilling4, the technique of manual osteotomes, manual compactors5, and, more recently, mechanized osseodensification6,7,8.

The osseodensification technique with rotary instruments was proposed as an alternative to other techniques, being able to compact and/or expand the bone tissue in a less traumatic way and with greater precision7. The osseodensification effect is due to the drill design. It presents many faces and a negative cutting angle, possibly increasing bone density while expanding the bone tissue during osteotomy8. Thus, these drills' design promotes compaction of the bone tissue, increasing its density laterally and, apically, improving the initial stability of the implant4,5,6,7,8. This fact can be observed in preclinical and clinical studies, which showed favorable results after applying the technique7,9,10.

On the other hand, the drills for osseodensification have a universal design, and their use is adapted according to the design (macrogeometry) of each implant system11,12. It can interfere negatively with the initial stability values. In this sense, using instruments manufactured with an adjusted design, which corresponds to the implant, may be more appropriate12.

However, since ossedensification drills are not sharp, irrigation during drilling must be abundant not to generate excessive heating13. High-temperature variation during osteotomy can cause undesirable bone tissue effects, possibly triggering peri-implantitis and implant loss (without osseointegration). Several factors are related to the increase in temperature during the osteotomy, such as drilling depth, drill design and sharpening, bone density, drilling speed, manual pressure applied, intermittent or continuous movements, and irrigation14,15,16,17. Gehrke et al.17 recently showed that bone healing is directly related to the trauma generated during the osteotomy and implant insertion torque18,19. The maintenance of adequate temperature levels can be achieved mainly with irrigation. This point has been approached by some companies that have developed mechanisms to improve and make the drills cooler during bone preparation, such as creating a specific device coupled to the drill, which is accelerated when the drill is activated20. However, adequate temperatures can be achieved via using low rotation speeds21. Moreover, as recently demonstrated by Achour et al.21, the use of drills with adequate cutting and speed can make a big difference for the collection of bone particles and subsequent use of this tissue to be used as material to fill gaps during the installation of implants.

The osseodensification technique using rotary instruments considered relatively recent, has few studies assessing the temperature variation during the procedure and no evidence of the ideal drill design22. Thus, the purpose of the present study was to evaluate the effects on the temperature and torque of a drill for osteotomy rotating counterclockwise to perform osseodensification. This in vitro study used blocks of synthetic low-density bone (types III and IV). Temperature variation during osteotomy (with and without irrigation) and maximum torque values during socket preparation were obtained and compared. The null hypothesis was that using the bur in a counterclockwise direction would not cause a significant increase in the local temperature variation during bed preparation for implant placement.

Two hundred forty (n = 240) osteotomies in polyurethane foam blocks (PFB). The PFB are standardized material for testing instruments and endosseous implants by the ASTM (American Society for Testing and Materials)23. The PFB at 0.320 g/cm3 (PCF 20), simulating low bone density (bone type III), and PFB at 0.160 g/cm3 (PCF 10), simulating an extra-low bone density (bone type IV), were used. Both blocks with a cortical portion of 1 mm at 0.640 g/cm3 (PCF 40), simulating a bone density type I. The blocks' dimensions were 95 × 45 × 35 mm (Nacional Ossos, Jaú, Brazil). These block models simulating the different types of bone density were used in other recent studies published by our group4,12. The thermal conductivity of the standardized synthetic block is 0.3 W/mK, which is analogous to the human cortical bone (0.29 W/m/K)24. These thermal conductivity values assured that the measured thermal variation in this block was equivalent to those in human bone25. Figure 1 shows an image of both synthetic bone blocks used.

Representative image of the two synthetic bone blocks used in the present study.

All osteotomies were performed using a single drill (TURBOdrill®, Implant Diffusion International, Montreuil, France) for a conical implant of 4.2 × 10 mm (diameter × length) at a recommended speed of 1500 rpm. Two groups were created following the osteotomy technique performed: conventional drilling (CD group) using the TURBOdrill in clockwise rotating and osseodensification drilling (OD group) using the TURBOdrill in initial clockwise rotating until perforating the cortical bone (~ 3 mm), and counterclockwise for the rest of the osteotomy depth. Each drill was used 20 times, that is, for each situation (four subgroups, two types of synthetic bone and torque test) a new drill was used, totaling 12 drills. Figure 2 shows an image of the TURBOdrill used.

The image shows the TURBOdrill details.

Regarding the design of the cutting edges, the TURBOdrill presents an acute angle on one side of its cutting blades that rotate clockwise, a slight inclination on the edge and a slight rounding on the second edge (after the cutting edge), as shown in Fig. 3.

Image showing the shape of the TURBOdrill cutting blades. The black arrows show the sharp angle for clockwise cutting, and the green arrows show the more rounded, lower design of the trailing edge of the blade. Yellow arrow showing clockwise rotation direction.

Both groups were tested under two conditions. The first condition (c1) was to make the osteotomies without irrigation, and the second condition (c2) was to perform the osteotomies using an intense irrigation of 50 mL/min with distilled water at room temperature (19 ± 1 °C). Thus, four subgroups were formed for the evaluations: CDc1, CDc2, ODc1, and ODc2.

For each subgroup, one synthetic bone block and one new drill were used, with a total of 20 osteotomies being performed for each subgroup. Firstly, the position of each osteotomy was marked on the model; then, we could make the lateral perforations where the 2 type K sensors (Mod. TP-01, Lutron Electronics Co., Inc., Coopersburg, PA, USA) were installed to measure the temperature during drilling. These perforations were made using a spherical carbide bur (1 mm in diameter and 2 mm in depth), calculating the distance of these perforations at 1 mm from the final diameter of the main drilling (osteotomy), as shown schematically in Fig. 4. The temperature variation depends on the density of the material, therefore the measurements were made in the cortical portion, where the density is greater and the values of temperature variation are greater, as demonstrated in a previous study16.

(a) Image of the TURBOdrill positioned to start the osteotomy and the thermocouple type k installed in the perforation. (b) Image after the osteotomy finished indicating the distance at 1 mm of the sensor.

For the osteotomies, an automated system machine for drilling was used. This apparatus was used in other previous studies14,16,20, which permitted to control of the drilling parameters (speed, the load applied, irrigation volume, and with/without intermittent movements). The parameter values used in our study were: 2 kg of load, intermittent movements (4, 8, and 10 mm), and irrigation of 50 mL/min (in condition c2). The temperature measured before starting drilling (iT) and the maximum temperature (mT) measured during the procedure was used to calculate the temperature variation (ΔT), which was used for comparative and statistical analyses. The maximum temperature reached during the entire processor was measured (initial to the end of the drilling, plus the time that the temperature began to decrease). Also, it is important to point out that after completing each drill, the following procedure was only performed after stabilizing the room temperature value.

Another 80 osteotomies were performed on both density blocks (n = 20 per group) to measure the maximum torque value during drilling. For this, a computerized drilling and torque measurement apparatus CME-30 nm (Técnica Industrial Oswaldo Filizola, São Paulo, Brazil) was used, keeping the same parameters of rotation speed (1500 rpm) and load (2 kg) and intermittent movements of the test anterior, however, without irrigation. The torque test was performed only without irrigation because the test machine does not allow liquid use. Figure 5 shows an image of the osteotomies and torque measurement apparatus.

The image shows the apparatus used to measure the maximum torque during the osteotomies.

Transversal cuts were performed in 3 bone blocks of each group in both types of density, randomly selected, to verify possible differences in density after performing each osteotomy technique. Images were taken using a stereo microscope (Wild Photomacroscope M400, Wild Leitz, Heerbrugg, Switzerland).

The data were compared statistically for both synthetic bone blocks using the ANOVA One-Way test to verify differences between the 2 groups in the 2 proposed conditions (without and with irrigation). In addition, Bonferroni's multiple comparison test was used to determine the difference between the 2 groups in the same condition and bone density in the same state but with different bone densities. GraphPad Prism version 5.01 for Windows (GraphPad Software, San Diego, CA, USA) was used to analyze the data, considering p < 0.05 as a statistically significant difference.

A total of 160 values of temperature variation, resulting from the difference between the maximum temperature and the initial temperature measured in each osteotomy was collected. The normality test (Kolmogorov–Smirnov test) was applied to these data, which detected a normal distribution within the groups.

Significant differences were detected when comparing the temperature variation in osteotomies with and without irrigation within each group and in the same type of bone density (p < 0.0001). Whereas comparing the data obtained between the groups under the same conditions (with or without irrigation and the same type of bone density), statistically significant differences were also detected. Table 1 presents the mean values (± standard deviation), confidence interval, and intra-group and inter-group statistical comparison of temperature variation. Figure 6 shows the distribution of these data using bar graphs.

Graphic showing ΔT during the osteotomies of both groups, in the 2 conditions proposed and 2 synthetic bone blocks.

A total of 80 peak torque values were computed and analyzed. In both bone densities, the torque values obtained in the CD group were significantly lower than those obtained during the proposed osseodensification procedure (OD). The mean values found were: 8.8 ± 0.97 N.cm for CD samples and 11.6 ± 1.08 N.cm for OD samples in the type III density bone; and 5.9 ± 0.99 N.cm for CD samples, and 9.6 ± 1.29 N.cm for OD samples in the type IV density bone (Fig. 7). When torque values were compared between the same groups but with different bone densities (type III vs. type IV), the values also showed statistically significant differences (p < 0.0001).

Box plots graphs showing the distribution of the maximum torque values measured during the osteotomies and the statistical comparison between both groups and the 2 synthetic bone blocks.

In the images obtained after cross-sections the blocks at both densities, it was possible to observe the compaction of the synthetic bone in the samples from the OD group, where the bur was used in a counterclockwise direction. While in the CD group samples, where the milling cutter was used in a clockwise direction, no increase in density was observed. Figure 8 presents images of both groups at both studied densities.

Representative images of both groups in both densities studied. In both cases was possible to observe the condensation of the medullary and cortical bone portion in the samples of the OD group compared to the CD group samples. Magnification of 10× and 100× , respectively.

This in vitro study aimed to assess the effects on the temperature and torque of a drill for osteotomy/densification rotating counterclockwise to promote osseodensification, with and without irrigation. Synthetic low-density bone blocks (types III and IV) were used to mimic the bones. The counterclockwise-rotation model for osteotomy preparation, known as the osseodensification technique, was designed using burs that promote lateralization of autogenous bone drilled into the surrounding cancellous structure, expanding the surrounding bone environment and increasing the local density. It can work on three different parameters: (i) it collects the bone dust and spreads them around the implant socket walls, increasing bone density and, consequently, the initial implant stability. This fact was significantly observed in our study (test groups)26,27; (ii) due to being a reverse drilling technique, it acts also effecting the alveolar ridge split28; and (iii) if used in the maxillary posterior area, the burs can push bone particles into the maxillary sinus, sinus lifting effect29.

The temperature variation and maximum torque were acquired using a bur rotating in a counterclockwise direction and were assessed and compared with conventional drilling in a clockwise direction. Our findings showed higher and more significant values for both parameters in the test group. Mishra & Chowdhary30 showed that the heat generated during the drilling process could have a multifactorial cause. Therefore, the authors suggested a drill speed of 2500 rpm with a force of 2–2.4 kg for osteotomy preparation, producing less heat. This fact was confirmed by Sharawy et al.31, who showed a safe drill speed at 2500 rpm with decreased risk of bony damage.

Moreover, that drill speed was evaluated for three years with reports superior of 99% for implant osseointegration, observing all bone-type densities31. In our study, we applied the rotation speed of 1500 rpm and a load of 2 kg in bones type III and IV, permitting a controllable temperature variance. Similar findings from Tehemar’s study32 stated that low hand pressure ranging around 2 kg, can be applied throughout the complete bony housing preparation with lesser heat. Moreover, the literature reported that temperatures exceeding 47 °C may result in bony necrosis due to thermal injury27. In concordance with that, a systematic review33 suggested that bone necrosis may happen in temperatures ranging between 47 and 55 °C when drilling for 1 min. Thereby, abundant irrigation is recommended, representing a simple solution for all bone drilling.

In addition, interruptions in the drilling procedure (at least every 5 s for 10 s) can dramatically decrease the chance of elevated temperatures30, and reusing drills more than 50 times can be another factor for bone heating and excessive damage to the tissue, impairing the osseointegration process34. This point was confirmed by Allsobrook et al.35, who suggested that drills can be used for up to 50 osteotomies without elevating temperatures and be harmful.

Regarding cell viability or better bone activity, some authors had higher and favorable results after using manual instruments or low-speed drilling (200 rpm, without irrigation) compared to the standard implant drilling process (speed > 800 rpm with copious irrigation)36. On the other hand, slower rotational speeds require more drilling time, which may produce more frictional heat. However, Reingewirtz et al.37 found a positive correlation between the temperature rise and the rotation speed. They tested a speed of 600 rpm, and it reduced the heat temperature during bone cutting and the drill speeds in dense bone.

The irrigation system, mainly using copious amounts of saline solution, has shown effective results for cooling for decades38. External cooling is considered the best option for cooling at superficial drill hole levels. Otherwise, in deeper holes, the internal system for cooling is a better choice. In our study, we used the traditional external system irrigation, similarly for all groups. Therefore, a combination of external and internal cooling seems beneficial, particularly in drilling compact bone sensitive to heat14,39.

Many methods can be used to measure the temperature generated during drilling. One of them was the real-time infrared thermography, which expresses the results by color on a monitor40,41; another is a shielded thermocouple, with a microprocessor thermometer recording the data obtained31,35,37,42,43,44; or using a digital thermometer for quantification of the temperature34, similarly used in this study. Reingewirtz et al.37 and Eriksson and Adell44 used one thermocouple with favorable results, whereas Sharawy31 evaluated through four thermocouples to monitor the temperature from different spots surrounding the site of drilling, which can be considered more precise.

As previously described, the conductivity values of the synthetic polyurethane blocks used in the present study present a low coefficient of thermal conductivity, which results in a heat accumulation right in front of the cutting edges45. Then, the sensor was installed as close as possible to the perforation site and, even at the end of each osteotomy, it was kept in position until the temperature value started to decrease.

A direct correlation was observed regarding the drilling torque tested in two different types of bone (types III and IV): the higher the bone density, the higher the drilling torque, similar to results reported in the literature46. Nonetheless, greater values were found for the osseodensification drilling (OD group) using the TURBOdrill counterclockwise for both bones. The torques across different bone densities indicate that the instrument responds to bone density similarly to how implant insertion torques will behave46. Moreover, even though the level of force can be significantly reduced with an increase in the number of revolutions of the drill due to a decrease in mean friction between the drills and the bone47, our study kept this variable constant.

Then, it is possible to conclude that using the drill counterclockwise for osseodensification in low-density bone generated a significantly greater torque and higher temperature variation during osteotomies, rejecting the null hypothesis between conventional and osseodensification drilling. However, the temperature range displayed by the OD group was below critical levels that can cause damage to bone tissue.

All data generated or analyzed during this study are included in this published article.

French, D., Ofec, R. & Levin, L. Long term clinical performance of 10 871 dental implants with up to 22 years of follow-up: A cohort study in 4247 patients. Clin. Implant. Dent. Relat. Res. 23(3), 289–297 (2021).

Article PubMed PubMed Central Google Scholar

Fernandes, G. V. O., Costa, B. M. G. N., Trindade, H. F., Castilho, R. M. & Fernandes, J. C. H. Comparative analysis between extra-short implants (≤6 mm) and 6 mm-longer implants: A meta-analysis of randomized controlled trial. Aust. Dent. J. 67(3), 194–211 (2022).

Article PubMed Google Scholar

Fernandes, P. R. E. et al. Clinical performance comparing titanium and titanium-zirconium or zirconia dental implants: A systematic review of randomized controlled trials. Dent. J. 10, 83 (2022).

Article Google Scholar

Gehrke, S. A. et al. Effects of the healing chambers in implant macrogeometry design in a low-density bone using conventional and undersized drilling. J. Int. Soc. Prev. Commun. Dent. 11(4), 437–447 (2021).

Google Scholar

Barberá-Millán, J. et al. Evaluation of the primary stability in dental implants placed in low density bone with a new drilling technique, Osseodensification: An in vitro study. Med. Oral Patol. Oral Cir Bucal. 26(3), e361–e367 (2021).

Article PubMed Google Scholar

Mello-Machado, R. C. et al. Osseodensification enables bone healing chambers with improved low-density bone site primary stability: An in vivo study. Sci. Rep. 11(1), 15436 (2021).

Article CAS PubMed PubMed Central Google Scholar

Trisi, P., Berardini, M., Falco, A. & Podaliri Vulpiani, M. New Osseodensification implant site preparation method to increase bone density in low-density bone: In vivo evaluation in sheep. Implant Dent. 25(1), 24–31 (2016).

Article PubMed PubMed Central Google Scholar

Seo, D.-J., Moon, S.-Y., You, J.-S., Lee, W.-P. & Oh, J.-S. The effect of under-drilling and osseodensification drilling on low-density bone: A comparative ex vivo study. Appl. Sci. 12(3), 1163 (2022).

Article CAS Google Scholar

Gaikwad, A. M., Joshi, A. A. & Nadgere, J. B. Biomechanical and histomorphometric analysis of endosteal implants placed by using the osseodensification technique in animal models: A systematic review and meta-analysis. J. Prosthet. Dent. 127(1), 61–70 (2022).

Article CAS PubMed Google Scholar

Bergamo, E. T. P. et al. Osseodensification effect on implants primary and secondary stability: Multicenter controlled clinical trial. Clin. Implant Dent. Relat. Res. 23(3), 317–328 (2021).

Article PubMed PubMed Central Google Scholar

Delgado-Ruiz, R., Gold, J., Somohano Marquez, T. & Romanos, G. Under-drilling versus hybrid osseodensification technique: Differences in implant primary stability and bone density of the implant bed walls. Materials 13(2), 390 (2020).

Article ADS PubMed PubMed Central Google Scholar

Formiga, M. C., Gehrke, A. F., De Bortoli, J. P. & Gehrke, S. A. Can the design of the instruments used for undersized osteotomies influence the initial stability of implants installed in low-density bone? An in vitro pilot study. PLoS ONE 16(10), e0257985 (2021).

Article Google Scholar

Bhargava, N. et al. Comparison of heat production and bone architecture changes in the implant site preparation with compressive osteotomes, osseodensification technique, piezoelectric devices, and standard drills: an ex vivo study on porcine ribs. Odontology 111(1), 142–153 (2023).

Article CAS PubMed Google Scholar

Gehrke, S. A., Loffredo Neto, H. & Mardegan, F. E. Investigation of the effect of movement and irrigation systems on temperature in the conventional drilling of cortical bone. Br. J. Oral Maxillofac. Surg. 51(8), 953–957 (2013).

Article PubMed Google Scholar

Chauhan, C. J., Shah, D. N. & Sutaria, F. B. Various bio-mechanical factors affecting heat generation during osteotomy preparation: A systematic review. Indian J. Dent. Res. 29(1), 81–92 (2018).

Article PubMed Google Scholar

Gehrke, S. A. et al. The influence of drill length and irrigation system on heat production during osteotomy preparation for dental implants: An ex vivo study. Clin. Oral Implants Res. 29(7), 772–778 (2018).

Article PubMed Google Scholar

Gehrke, S. A., Treichel, T. L. E., Aramburú Júnior, J., de Aza, P. N. & Prados-Frutos, J. C. Effects of the technique and drill design used during the osteotomy on the thermal and histological stimulation. Sci. Rep. 10(1), 20737 (2020).

Article CAS PubMed PubMed Central Google Scholar

Gehrke, S. A. et al. Effects of insertion torque values on the marginal bone loss of dental implants installed in sheep mandibles. Sci. Rep. 12(1), 538 (2022).

Article ADS CAS PubMed PubMed Central Google Scholar

Gehrke, S. A. et al. Randomized clinical trial comparing insertion torque and implant stability of two different implant macrogeometries in the initial periods of osseointegration. Medicina 59(1), 168 (2023).

Article PubMed PubMed Central Google Scholar

Gehrke, S. A. et al. Development of a new drill design to improve the temperature control during the osteotomy for dental implants: A comparative in vitro analysis. Biology 9(8), 208 (2020).

Article CAS PubMed PubMed Central Google Scholar

Ben Achour, A. et al. The influence of thrust force on the vitality of bone chips harvested for autologous augmentation during dental implantation. Materials 12(22), 3695 (2019).

Article ADS PubMed PubMed Central Google Scholar

Delgado-Ruiz, R., Mahdian, M., Benezha, I. & Romanos, G. Counterclockwise drilling with different tapered drills condenses the implant bed-an optical coherence tomography in vitro study. Medicina 57(9), 940 (2021).

Article PubMed PubMed Central Google Scholar

ASTM F1839-08. Standard Specification for Rigid Polyurethane Foam for Use as a Standard Material for Testing Orthopaedic Devices and Instruments. (ASTM International, West Conshohocken, 2016).

Clattenburg, R., Cohen, J., Conner, S. & Cook, N. Thermal properties of cancellous bone. J. Biomed. Mater. Res. 9(2), 169–182 (1975).

Article CAS PubMed Google Scholar

Strbac, G. D. et al. A novel standardized bone model for thermal evaluation of bone osteotomies with various irrigation methods. Clin. Oral Implants Res. 25(5), 622–631 (2014).

Article PubMed Google Scholar

Bergamo, E. T. et al. Osseodensification effect on implants primary and secondary stability: Multicenter controlled clinical trial. Clin. Implant Dent. Relat. Res. 23, 317–328 (2021).

Article PubMed PubMed Central Google Scholar

Huwais, S. & Meyer, E. G. A novel osseous densification approach in implant osteotomy preparation to increase biomechanical primary stability, bone mineral density, and bone-to-implant contact. Int. J. Oral Maxillofac. Implants. 32, 27–36 (2017).

Article PubMed Google Scholar

Koutouzis, T. et al. Alveolar ridge expansion by osseodensification-mediated plastic deformation and compaction autografting: A multicenter retrospective study. Implant Dent. 28, 349–355 (2019).

Article PubMed Google Scholar

Salgar, N. Osseodensified crestal sinus window augmentation: an alternative procedure to the lateral window technique. J. Oral Implantol. 47, 45–55 (2021).

Article PubMed Google Scholar

Mishra, S. K. & Chowdhary, R. Heat generated by dental implant drills during osteotomy - A review. J. Indian Prosthodont. Soc. 14(2), 131–143 (2014).

Article CAS PubMed PubMed Central Google Scholar

Sharawy, M., Misch, C., Weller, N. & Tehemar, S. Heat generation during implant drilling: The significance of motor speed. J. Oral Maxillofac. Surg. 60, 1160–1169 (2002).

Article PubMed Google Scholar

Tehemar, S. H. Factors affecting heat generation during implant site preparation: A review of biologic observations and future considerations. Int. J. Oral Maxillofac. Implants. 14, 127–136 (1999).

CAS PubMed Google Scholar

Kniha, K. et al. Temperature threshold values of bone necrosis for thermo-explantation of dental implants - A systematic review on preclinical in vivo research. Materials 13(16), 3461 (2020).

Article ADS CAS PubMed PubMed Central Google Scholar

de Souza Carvalho, A. C. G. et al. Evaluation of bone heating, immediate bone cell viability, and wear of high-resistance drills after the creation of implant osteotomies in rabbit tibias. Int. J. Oral Maxillofac. Implants. 26, 1193–1201 (2011).

Google Scholar

Allsobrook, O. F. L., Leichter, J., Holborow, D. & Swain, M. Descriptive study of the longevity of dental implant surgery drills. Clin. Implant Dent. Relat. Res. 13(3), 244–254 (2011).

Article PubMed Google Scholar

Tabassum, A., Wismeijer, D., Hogervorst, J. & Tahmaseb, A. Comparison of proliferation and differentiation of human osteoblast-like cells harvested during implant osteotomy preparation using two different drilling protocols. Int. J. Oral Maxillofac. Implants. 35, 141–149 (2020).

Article PubMed Google Scholar

Reingewirtz, Y., Szmukler-Moncler, S. & Senger, B. Influence of different parameters on bone heating and drilling in implantology. Clin. Oral Implant Res. 8, 189–197 (1997).

Article CAS Google Scholar

Eriksson, R. & Albrektsson, T. Temperature threshold levels for heat induced bone tissue injury: A vital-microscopic study in the rabbit. J. Prosthet. Den. 50, 101–107 (1983).

Article CAS Google Scholar

Haider, R., Watzek, G. & Plenk, H. Effects of drill cooling and bone structure on imz implant fixation. Int. J. Oral Maxillofac. Implants. 8, 83–91 (1993).

CAS PubMed Google Scholar

Watanbe, F., Tawada, Y., Komatsu, S. & Hata, Y. Heat distribution in bone during preparation of implant sites: heat analysis by real-time thermography. Int. J. Oral. Maxillofac. Implants. 7, 212–219 (1992).

Google Scholar

Jun, Oh. H. et al. Effect of implant drill characteristics on heat generation in osteotomy sites: A pilot study. Clin. Oral. Implants Res. 22, 722–726 (2011).

Article Google Scholar

Chacon, G. E., Bower, D. L., Larsen, P. E., McGlumphy, E. A. & Beck, F. M. Heat production by 3 implant drill systems after repeated drilling and sterilization. J. Oral Maxillofac. Surg. 64, 265–269 (2006).

Article PubMed Google Scholar

Brisman, D. The effect of speed, pressure, and time on bone temperature during the drilling of implant sites. Int. J. Oral Maxillofac. Implants. 11, 35–37 (1996).

CAS PubMed Google Scholar

Eriksson, R. & Adell, R. Temperatures during drilling for the placement of implants using the osseointegration technique. J. Oral Maxillofac. Surg. 44, 4–7 (1986).

Article CAS PubMed Google Scholar

Islam, M. A. et al. A review of surgical bone drilling and drill bit heat generation for implantation. Metals 12(11), 1900 (2022).

Article CAS Google Scholar

Velikov, S., Susin, C., Heuberger, P. & Irastorza-Landa, A. A new site preparation protocol that supports bone quality evaluation and provides predictable implant insertion torque. J. Clin. Med. 9, 494. https://doi.org/10.3390/jcm9020494 (2020).

Article PubMed PubMed Central Google Scholar

Alam, K., Mitrofanov, A. V. & Silberschmidt, V. V. Experimental investigations of forces and torque in conventional and ultrasonically-assisted drilling of cortical bone. Med. Eng. Phys. 33(2), 234–239 (2011).

Article CAS PubMed Google Scholar

Download references

The author Sergio Alexandre Gehrke was funded by post-doctoral grant nº 2021/PER/00020 from the Ministerio de Universidades under the program "Ayudas para la recualificación del sistema universitario español de la Universidad Miguel Hernandez" modalidad "Margarita Salas para la formación de jóvenes doctores". The funders had no role in study design, data collection and analysis, decision to publish, or preparation of the manuscript.

Part of this work was supported by the Ministry of Science and Innovation—Grant PID2020-116693RB-C21 funded by MCIN/AEI/https://doi.org/10.13039/501100011033.

Associate Professor et Department of Cariology and Comprehensive Care, New York University, New York, NY, 10010, USA

Raphael Bettach

Paris, France

Gilles Boukhris & Sergio Alexandre Gehrke

Instituto de Bioingenieria, Universidad Miguel Hernández de Elche, Alicante, Spain

Piedad N. De Aza

Department of Materials Engineering, Pontificial Catholic University of Rio Grande do Sul, Porto Alegre, Brazil

Eleani Maria da Costa & Sergio Alexandre Gehrke

Department of Innovative Technologies in Medicine and Dentistry, University of Chieti-Pescara, 66100, Chieti, Italy

Antonio Scarano

Department of Research, Bioface/PgO/UCAM, Calle Cuareim 1483, 11100, Montevideo, Uruguay

Antonio Scarano & Sergio Alexandre Gehrke

Periodontics and Oral Medicine Department, University of Michigan School of Dentistry, Ann Arbor, MI, 48109, USA

Gustavo Vicentis Oliveira Fernandes

Department of Biotechnology, Universidad Católica de Murcia (UCAM), Murcia, Spain

Sergio Alexandre Gehrke

You can also search for this author in PubMed Google Scholar

S.A.G., R.B., G.B. and A.S. made the experimental analysis; S.A.G, G.V.O.F. and P.N.A. made the analysis; S.A.G. and E.M.C. wrote the main manuscript text and S.A.G. prepared figures 1–6. All authors reviewed the manuscript.

Correspondence to Sergio Alexandre Gehrke.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Bettach, R., Boukhris, G., De Aza, P.N. et al. New strategy for osseodensification during osteotomy in low-density bone: an in vitro experimental study. Sci Rep 13, 11924 (2023). https://doi.org/10.1038/s41598-023-39144-z

Download citation

Received: 23 February 2023

Accepted: 20 July 2023

Published: 24 July 2023

DOI: https://doi.org/10.1038/s41598-023-39144-z

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.